“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.
Analysis of phase change phenomenain multicomponent systems with aspects of technical applying
[I. Vušanović]
PDF/A (209 pages)
Prostiranje toplote i mase/ Transport phenomena
Datum odbrane: 12.03.2002
Voronjec, Dimitrije (mentor)
Krane, Matthew J. (komentor)
Radmilović, Velimir (član komisije)
Vukoslavčević, Petar, 1949- (član komisije)
Kažić, Nenad, 1946- (član komisije)
Tokom solidifikacije legura metala dolazi do stvaranja odredjenih nepravilnosti u strukturi metala koji su direktna posledica transportnih procesa koji se odigravaju tokom procesa livenja legure. Kao jedan od najvažnijih nepovoljnih fenomena koji se odigrava može se navesti redistribucija (segregacija) legirajućih elemenata, koja je posledica strujanja u fluidu tokom procesa očvršćavanja sa jedne strane, i fizike‘procesa očvršćavanja koje je praćeno promjenom masenog sastava legirajućih elemenata u čvrstim fazama i u tečnosti. Kao početna osnova za istraživanje poslužili su razvijeni kontinuum modeli za binarne strukture, koji su prošireni uključivanjem u razmatranje treće komponente. Fazni dijagram trokomponentne legure Al-Cu-Mg koji je opisan trostranom pravilnom prizmom sa temperaturom kao aksijal- nom koordinatom i osnovom koju čine binarni dijagrami elemenata legure, opisan je posebnim setom jednačina kojima se opisuju procesi u primarnoj, sekundarnoj i eutektičkoj reakciji. Srednje vrijednosti masenih udjela bakra i magnezijuma u fazama sračunavaju se računanjem integralnih vrijednosti iz dobijenih profila masenih sastava bakra i magnezijuma u fazama.
Sa razvijenim mikrosegregacionim i makrosegregacionim modelom sproveden je niz numeričkih eksperimenata u cilju sagledavanja razlika izmedju različitih pristupa u tretiranju difuzije legirajućih bakra i magnezijuma u primarnoj fazi. Rezultati mikrosegregacinih analiza uporedjeni su sa rezultatima eksperimenta dostupnim iz literature, i prikazane su dobre i loše strane modela. Numerički eksperimenti sa kojima je opisan fenomen makrosegregacije za četiri odabrane legure pokazali su razlike izmedju različitih pristupa u tretiranju fenomena difuzije u primarnoj fazi. Eksperimentalnim istraživanjem odredjeni su elementi trenzora difuzije legirajućih bakra i magnezijuma u primarnom aluminij umu. Analize su pokazale da koeficijenti difuzije nisu konstantne vrijednosti već da zavise od atomskih koncentracija legirajućih elemenata.
During solidification of alloys some defects can arise influenced by transport phenom- ena, which occurs in process. On such defect is the redistribution (segregation) of alloying elements, which is followed by changing of compositions in solid and liquid phase. Using the continuum model as a basis approach, existing continuum model was extended in order to in- clude third component. Phase diagram of Al-Cu-Mg three component alloy which is described as regular triangular prism with temperature as axial coordinate and base which is contained from three different binary diagrams, was described with different sets of equations for pri- mary, secondary and ternary reaction. Average compositions of cooper and magnesium in ali phases was calculated using the values from the composition profiles, which are generated during the solidification.
With microsegregation and macrosegregation codes couple of calculations are per- formed in order to considering different approaches in treatment of diffusion of cooper and magnesium in solids. Results of microsegregation analysis are compared with existing experi- mental results and some disadvantages of exposed model are shown. Numerical experiments for chosen four alloys shows differences between equilibrium approach and approach with and without diffusion in primary phase. Experimental analysis has performed in order to de- termine elements of diffusion tensor of cooper and magnesium in primary aluminum. Experimental result shows there is a some influence on diffusion coefficients from atomic con- centration of alloying elements.
Tokom solidifikacije legura metala dolazi do stvaranja odredjenih nepravilnosti u strukturi metala koji su direktna posledica transportnih procesa koji se odigravaju tokom procesa livenja legure. Kao jedan od najvažnijih nepovoljnih fenomena koji se odigrava može se navesti redistribucija (segregacija) legirajućih elemenata, koja je posledica strujanja u fluidu tokom procesa očvršćavanja sa jedne strane, i fizike‘procesa očvršćavanja koje je praćeno promjenom masenog sastava legirajućih elemenata u čvrstim fazama i u tečnosti. Kao početna osnova za istraživanje poslužili su razvijeni kontinuum modeli za binarne strukture, koji su prošireni uključivanjem u razmatranje treće komponente. Fazni dijagram trokomponentne legure Al-Cu-Mg koji je opisan trostranom pravilnom prizmom sa temperaturom kao aksijal- nom koordinatom i osnovom koju čine binarni dijagrami elemenata legure, opisan je posebnim setom jednačina kojima se opisuju procesi u primarnoj, sekundarnoj i eutektičkoj reakciji. Srednje vrijednosti masenih udjela bakra i magnezijuma u fazama sračunavaju se računanjem integralnih vrijednosti iz dobijenih profila masenih sastava bakra i magnezijuma u fazama.
Sa razvijenim mikrosegregacionim i makrosegregacionim modelom sproveden je niz numeričkih eksperimenata u cilju sagledavanja razlika izmedju različitih pristupa u tretiranju difuzije legirajućih bakra i magnezijuma u primarnoj fazi. Rezultati mikrosegregacinih analiza uporedjeni su sa rezultatima eksperimenta dostupnim iz literature, i prikazane su dobre i loše strane modela. Numerički eksperimenti sa kojima je opisan fenomen makrosegregacije za četiri odabrane legure pokazali su razlike izmedju različitih pristupa u tretiranju fenomena difuzije u primarnoj fazi. Eksperimentalnim istraživanjem odredjeni su elementi trenzora difuzije legirajućih bakra i magnezijuma u primarnom aluminij umu. Analize su pokazale da koeficijenti difuzije nisu konstantne vrijednosti već da zavise od atomskih koncentracija legirajućih elemenata.